C-PAK TYPE CA-1013 CLEAR CARRIER TAPE UTILISES SPECIALLY FORMULATED CLEAR STATIC DISSIPATIC POLYSTYRENE GIVING CONSISTENT SEALING STRENGTH WITH ITS SMOOTH AND FLAT FLANGE SURFACE.
EMBOSSING
OF CARRIER TAPE IS ON HIGH END MACHINES AND WITH C-PAK’S ESPECIALLY DEVELOPED
PROCESSES TO ENSURE PRECISE DIMENSIONS AND WELL DEFINED POCKETS SUITABLE FOR
HIGH-SPEED AUTOMATED TAPING AND SURFACE MOUNT EQUIPMENT.
GENERAL PROPERTIES* ( TYPICAL
VALUE ONLY )
|
|
|
METHOD |
VALUE |
|
|
|
|
|
|
SPECIFIC GRAVITY |
|
ASTM D-792 |
1.085 g/cm3 |
|
|
|
|
|
|
TENSILE @ YIELD |
MD |
ASTM D-882 |
4.3 kg/mm2 |
|
|
TD |
|
4.1 kg/mm2 |
|
|
|
|
|
|
ELONGATION @ BREAK |
MD |
ASTM D-882 |
29% |
|
|
TD |
|
23% |
|
|
|
|
|
|
TEAR STRENGTH |
MD |
ASTM D-1004 |
1.7 kg/mm2 |
|
|
TD |
|
1.6 kg/mm2 |
|
|
|
|
|
|
LIGHT TRANSMITTANCE |
|
ASTM D-1003 |
90 % |
|
|
|
|
|
|
*APPLICABLE ON RAW MATERIAL |
|
|
|
|
ELECTRICAL PROPERTIES |
|
|
|
|
|
|
|
|
|
SURFACE RESISTIVITY |
|
ASTM D-257 |
1010 ohms/sq |
|
|
|
|
|
|
STATIC DECAY TIME (+/-5KV AT 10% CUTOFF) |
|
EIA-541 |
≤0.07 sec |
|
|
|
|
|
|
TRIBOELECTRIC CHARGE |
|
EIA-541 |
≤30 volt |
|
|
|
|
|
|
Material Ionic
Data |
|
|
|
|
Four Heavy Metals |
PPM |
|
|
|
Cadmium (Cd) |
< 2 |
|
|
|
Lead (Pb) |
< 2 |
|
|
|
Mercury (Hg) |
< 2 |
|
|
|
Hexavalent Chromium (Cr+6) |
< 2 |
|
|
|
|
|
|
|
|
** The ionic data was measured by an Independent Laboratory. |
|
||
|
|
|
|
|